Generic Nylon 66/6
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B2Gi8M_Generic-Nylon-66-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66/6 This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 - 1.14 | g/cm³ | ASTM D792 |
| 23°C | 1.11 - 1.17 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 - 0.78 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 1.2 - 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.60 - 2.5 | % | ASTM D955 |
| 23°C | 0.70 - 2.2 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 1.1 - 1.7 | % | ASTM D570 |
| 23°C, 24 hr | 1.1 - 1.6 | % | ISO 62 |
| Saturated, 23°C | 9.0 | % | ASTM D570 |
| Saturated, 23°C | 7.9 - 11 | % | ISO 62 |
| Equilibrium, 23°C | 2.5 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.5 - 3.5 | % | ISO 62 |
| Viscosity Number | 138 - 247 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 77 - 80 | ISO 868 | |
| Ball Indentation Hardness | 45.0 - 201 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 477 - 10500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 64.8 - 85.4 | MPa | ASTM D638 |
| Yield, 23°C | 39.1 - 89.3 | MPa | ISO 527-2 |
| Fracture, 23°C | 79.5 - 85.0 | MPa | ASTM D638 |
| Fracture, 23°C | 40.0 - 172 | MPa | ISO 527-2 |
| 23°C | 38.6 - 73.4 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 3.0 - 21 | % | ISO 527-2 |
| Fracture, 23°C | 3.0 - 77 | % | ASTM D638 |
| Fracture, 23°C | 2.2 - 12 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 5.6 - 50 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 800 - 3670 | MPa | ASTM D790 |
| 23°C | 600 - 4920 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 51.5 - 131 | MPa | ASTM D790 |
| 23°C | 25.0 - 196 | MPa | ISO 178 |
| Coefficient of Friction | 0.30 - 1.0 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 - 21 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 48 - 110 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 35 - 76 | J/m | ASTM D256 |
| 23°C | 4.0 - 22 | kJ/m² | ISO 180 |
| Notched Izod Impact (23°C) | 9.00 - 28.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 184 - 225 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 69.6 - 221 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 66.8 - 93.6 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 55.0 - 91.0 | °C | ISO 75-2/A |
| Continuous Use Temperature | 87.0 - 203 | °C | ASTM D794 |
| Vicat Softening Temperature | 68.0 - 248 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 199 - 250 | °C | |
| -- | 193 - 260 | °C | ISO 11357-3 |
| -- | 190 - 257 | °C | ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 6.9E-5 - 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 6.9E-5 - 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 - 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 2.5E+13 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 55 - 1.1E+15 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+4 - 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 17 - 26 | kV/mm | ASTM D149 |
| 23°C | 17 - 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 3.50 | IEC 60250 | |
| Dissipation Factor (23°C) | 0.020 - 0.30 | IEC 60250 | |
| Comparative Tracking Index | 497 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 952 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 743 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 - 28 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.8 - 93.0 | °C | |
| Drying Time | 2.7 - 7.4 | hr | |
| Suggested Max Moisture | 0.12 - 0.27 | % | |
| Rear Temperature | 236 - 270 | °C | |
| Middle Temperature | 254 - 278 | °C | |
| Front Temperature | 257 - 276 | °C | |
| Processing (Melt) Temp | 233 - 281 | °C | |
| Mold Temperature | 59.9 - 80.9 | °C | |
| Injection Pressure | 8.00 - 90.8 | MPa | |
| Holding Pressure | 6.85 - 30.8 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66/6This information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.6 - 80.0 | °C | |
| Suggested Max Moisture | 0.080 - 0.081 | % | |
| Cylinder Zone 1 Temp. | 238 | °C | |
| Cylinder Zone 2 Temp. | 238 | °C | |
| Cylinder Zone 3 Temp. | 238 | °C | |
| Cylinder Zone 4 Temp. | 238 | °C | |
| Melt Temperature | 248 | °C | |
| Die Temperature | 240 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66/6This information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 6634F | Formosa Plastics Corporation | LDPE | TAISOX |
| Adell Polyamide BR-14 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| Huaxia Shenzhou DS606 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluoropolymer | Huaxia Shenzhou |
| Jiangsu Sinarise EX9735X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Hostacom TRC 103P G71322 | LyondellBasell Industries | PP Copolymer | Hostacom |