Trilene® RE20WL
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Trilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B1kgW8_Trilene-RE20WL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RE20WL is a polypropylene random copolymer for production of woven cloth & BOPP lamination. This grade uses Unipol® polypropylene technology with latest catalyst technology. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.895 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 65 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 15 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 730 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 65 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 3 |
| Peak Melting Temperature 4 | 144 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 270 - 320 | °C |
| Extrusion instructions |
|---|
| Cooling Temperature: 20 to 35°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 标准 B (120°C/h) |
| 4 . | 10°C/min, 2 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trithene® TS 8090 | Petroquimica Triunfo | LDPE | Trithene® |
| UMG ABS® VW801 | UMG ABS, Ltd. | ABS | UMG ABS® |
| Nipolon® Hard 8022 | TOSOH Corporation | HDPE | Nipolon® Hard |
| Complet® LCF50-PA6 | PlastiComp, Inc. | Nylon 6 | Complet® |
| Sylvin 6422-62 Natural | Sylvin Technologies Incorporated | TPE | Sylvin |