Vyncolit® RX®3-1-530 Datasheet,DAP,Vyncolit N.V.-SHANGHAI SUSHENG

Message
3-1-530 is a long glass fiber reinforced, flame retardant, diallyl ortho-phthalate molding compound, which meets the requirements of ASTM D5948 Type GDI-30F.

General Information
Filler / Reinforcement	Long glass fiber
Features	Good dimensional stability Moisture resistance Antibacterial property Solvent resistance Impact resistance, high Good electrical performance Good chemical resistance alkali resistance Good wear resistance Fuel resistance Heat resistance, high acid resistance Flame retardancy
Uses	Membrane key switch Aircraft applications Insulating material Connector Communication Equipment
Agency Ratings	ASTM D 5948, Type GDI-30F MIL C-24308
Appearance	Black Grey Green
Forms	flake
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.76	g/cm³	ASTM D792
Molding Shrinkage - Flow (Compression Molded)	0.10 - 0.40	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break, Compression Molded)	69.0	MPa	ASTM D638
Flexural Modulus (Compression Molded)	13800	MPa	ASTM D790
Flexural Strength (Break)	131	MPa	ASTM D790
Compressive Strength	152	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (Compression Molded)	160	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded)	260	°C	ASTM D648
CLTE - Flow	2.2E-5	cm/cm/°C	ASTM E831
RTI Elec	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI	130	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength ¹	16	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
1 kHz	4.10		ASTM D150
1 MHz	3.50		ASTM D150
Dissipation Factor			ASTM D150
1 kHz	0.010		ASTM D150
1 MHz	0.018		ASTM D150
Arc Resistance	130	sec	ASTM D495
Comparative Tracking Index (CTI)	600	V	UL 746
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.59 mm	V-0		UL 94
3.18 mm	V-0		UL 94
Oxygen Index	30	%	ASTM D2863

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	76.7	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	110 - 116	°C
Mold Temperature	160 - 182	°C

Injection instructions
Plastication: 50rpmBack Pressure (gauge): slightInjection Pressure: set to give 5 to 15 sec injection timeHold Pressure: 1/2 of injection pressureCure Time, 0.125 in: 40 secWater Absorption, ASTM D570, 48 hrs, 50°C: 0.35%Flammability Ignition, ASTM D229: 110 secFlammability Burn, ASTM D229: 40 secDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 15.8 kV/mmDielectric Constant, ASTM D150, 1000 Hz, wet: 4.1Dielectric Constant, ASTM D150, 1000000 Hz, wet: 3.5Dissipation Factor, ASTM D150, 1000 Hz, wet: 0.01Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.018Compression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 220 to 230 °F Preheat Time: 45 sec Mold Temperature: 320 to 350 °F Compression Mold Pressure: 3500 to 6000 psi Transfer Mold Pressure: 2500 to 5000 psi Cure Time, 0.125 in: 45 to 70 sec

Injection instructions

Plastication: 50rpmBack Pressure (gauge): slightInjection Pressure: set to give 5 to 15 sec injection timeHold Pressure: 1/2 of injection pressureCure Time, 0.125 in: 40 secWater Absorption, ASTM D570, 48 hrs, 50°C: 0.35%Flammability Ignition, ASTM D229: 110 secFlammability Burn, ASTM D229: 40 secDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 15.8 kV/mmDielectric Constant, ASTM D150, 1000 Hz, wet: 4.1Dielectric Constant, ASTM D150, 1000000 Hz, wet: 3.5Dissipation Factor, ASTM D150, 1000 Hz, wet: 0.01Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.018Compression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 220 to 230 °F Preheat Time: 45 sec Mold Temperature: 320 to 350 °F Compression Mold Pressure: 3500 to 6000 psi Transfer Mold Pressure: 2500 to 5000 psi Cure Time, 0.125 in: 45 to 70 sec

Note Message
1 .	Method B (step by step)

Category:	DAP , Diallyl Phthalate
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	B1Erit_Vyncolit-RX-3-1-530.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sinvicomp SGH6020	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Sinvicomp
SUSTAMID 6G M	Röchling Sustaplast SE & Co. KG	Nylon 6	SUSTAMID
LNP™ THERMOCOMP™ DC006ER compound	SABIC Innovative Plastics	PC	LNP™ THERMOCOMP™
Sylvin 8200-88 Blue 8420	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
LNP™ LUBRICOMP™ RAL22I compound	SABIC Innovative Plastics	Nylon 66	LNP™ LUBRICOMP™