EVAL™ LT174B
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B19bRR_EVAL-LT174B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 27 mol% Ethylene Vinyl Alcohol Copolymer LT174B - Pellets are lubricated to facilitate material feeding into extruder |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Ethylene Content | 27.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 44.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 16 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 0% RH | 2.8E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 5.1E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.031 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 1(40°C, 90% RH) | 1.7 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 2.0 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 60.0 | °C | ISO 11357-2 |
| Melting Temperature | 191 | °C | ISO 11357 |
| Peak Crystallization Temperature | 165 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® OF 600M | ELASTO | TPE | Mediprene® |
| Boda BDF60C | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| CALP 1420G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| LUVOCOM® 1850/GF/30/TF/13/SI/2 | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| Sylvin 7833-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |