PRL PPX-G20
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AzvQc6_PRL-PPX-G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-G20 is a Polyphenylene Ether + PS (PPE+PS) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 1.0 to 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 93.1 | MPa | |
| Break, 3.18 mm | 93.1 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 5170 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.3 | kJ/m² | ISO 179/1 |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 53 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 80 | J/m | ASTM D256 |
| 23°C | 6.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 132 | °C | |
| Vicat Softening Temperature | 143 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 271 to 310 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 71.1 to 104 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PL-1621 (Punching) | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| ALKAMIX™ MB-UV815 | Marplex Australia Pty. Ltd. | PE, Unspecified | ALKAMIX™ |
| Elastron® G G500.A30.B.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| LNP™ THERMOCOMP™ AF001H compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
| Sylvin 8980-60 White 1322 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |