Trilene® HI35HO
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Trilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Azng4n_Trilene-HI35HO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trilene HI35HO is an excellent high flow polypropylene homopolymer for thin-walled and multicavity household and fine denier spunbond non wovens fabrics. This grade uses Unipol® polypropylene technology, with latest catalyst technology. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.903 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 33.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1260 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 3 |
| Peak Melting Temperature 4 | 163 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | Rate B (120°C/h) |
| 4 . | 10°C/min, 2nd heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-FR2A-D | Polymer Resources Ltd. | PC | PRL |
| UNISOFT TPE™ ST-65A-BK-3-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Iupiace® GHF3010 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LNP™ THERMOCOMP™ UX06032-WH9E041 compound | SABIC Innovative Plastics Europe | PPA | LNP™ THERMOCOMP™ |
| Lupox® SG3250M | LG Chem Ltd. | PBT+PET | Lupox® |