TAROMID A 280 Z1 G6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AzauTh_TAROMID-A-280-Z1-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66 medium viscosity 30% glass fibres reinforced, elastomer modified, very good mechanical properties, good dimensional stability and low water absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 - 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.20 - 0.35 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.50 | % | ISO 62 |
| Saturated, 23°C | 4.5 | % | ISO 62 |
| Granule Humidity 1 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(750°C) | 30 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 8000 | MPa | ISO 178 |
| Flexural Stress 4 | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -25°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 90 | J/m | ASTM D256 |
| 23°C | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 215 | °C | ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 6 | 100 | °C | IEC 60216 |
| -- 7 | 140 | °C | IEC 60216 |
| Vicat Softening Temperature | 225 | °C | ISO 306/B50 |
| Ball Pressure Test (205°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 256 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 8.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | 20,000 hr, 130 H |
| 7 . | Short term, 180 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1670B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| Styropor® BFL 395 | BASF Corporation | PS (EPS) | Styropor® |
| Adstif HA5034 | PolyMirae | PP, High Crystal | Adstif |
| Delrin® FG100TL NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Sylvin 6231-90 Yellow 4196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |