RAMTOUGH PZ725
| Category: | PC , Polycarbonate |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMTOUGH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AxAob9_RAMTOUGH-PZ725.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UV STABILIZED AND IMPACT MODIFIED POLYCARBONATE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 21 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.80 | % | ASTM D955 |
| -- | 0.50 - 0.80 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.15 | % | ASTM D570 |
| Saturated, 23°C | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 66.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 140 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 2300 | MPa | ASTM D790 |
| -- | 2350 | MPa | ISO 178 |
| Flexural Strength | 100 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 680 | J/m | ASTM D256 |
| 23°C | 70 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 137 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 145 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ASTM D1525, ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Processing (Melt) Temp | 270 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® W5000 | Vyncolit N.V. | Phenolic | Vyncolit® |
| APEX® 1700-50 | Teknor Apex Company | PVC, Flexible | APEX® |
| Globalene® PF3006 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| KPOL-PP K-PPH 14.0 | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| KEBAFLEX® S 85 A.02 | BARLOG plastics GmbH | TES | KEBAFLEX® |