Hostacom ERC 236N
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AvSYYN_Hostacom-ERC-236N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom ERC 236N is a UV stabilised, 18 % mineral filled polypropylene copolymer for injection moulding. It combines a good flowability with good stiffness/impact properties. The grade has been specifically designed for molding of automotive interior trim parts. The grade is available in color-matched, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Flexural Modulus - Secant | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.5 | kJ/m² | |
| 23°C | 15 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANPRO® SM840 | Lotte Chemical Titan (M) Sdn. Bhd. | PP Impact Copolymer | TITANPRO® |
| NEXUS PC/PET PC/PET7901 | Nexus Resin Group, LLC. | PC+PET | NEXUS PC/PET |
| Axiall PVC 113B-FR | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Flontech® FT-1-5 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| LITEN ZB 29 | UNIPETROL RPA | PE Copolymer | LITEN |