Paryls® PSU F3150GL20
| Category: | PSU , Polysulfone |
| Manufacturer: | Youju New Materials Co., Ltd. |
| Trademark: | Paryls® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AvOLpO_ParylsPSUF3150GL20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PARYLS® PSU F3250GL20 pellets are supplied in cartons lining aluminum foil bag, which can be stored indefinitely, provided the packaging remains undamaged. PARYLS® PSU F3250GL20 pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 6h at 160 °C in a vacuum or dry air drier prior to processing. Features PARYLS® PSU F3250GL20, resin is a 20% glass fiber reinforced polysulfone(PSU). Glass fiber substantially increasee the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the polysulfone resin. The high performance properties make these resins particularly effective alternatives to metals in many engineering applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (343°C/2.16 kg) | 5.0 - 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4, ISO 2577 | ||
| Transverse flow | 0.50 | % | ISO 294-4, ISO 2577 |
| Flow | 0.30 | % | ISO 294-4, ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6800 | MPa | ISO 527-2 |
| Tensile Stress | 108 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.2 | % | ISO 527-2 |
| Flexural Modulus | 6400 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 184 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 185 | °C | ISO 11357-2, DSC |
| CLTE - Flow (23°C) | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity 3 | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength 4 | 46 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.50 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 6.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.0 mm | HB | UL 94 | |
| 4.5 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 160 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 350 - 390 | °C | |
| Mold Temperature | 130 - 180 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 160 | °C | |
| Drying Time | 6.0 | hr | |
| Melt Temperature | 350 - 390 | °C | |
| Die Temperature | 130 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 100V |
| 3 . | 100V |
| 4 . | K20/K20, (60*60*1 mm³) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® H707-12NSM | Safripol (PTY) LTD | PP Homopolymer | Safron® |
| Andur 74-AGP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Cleapact TS-50 E | DIC Corporation | PS Alloy | Cleapact |
| Impet® 2700 GV1/30 | Celanese Corporation | PET | Impet® |
| Karina BLACK PVC COMPOUND 880-48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |