TEKANATE™ G7020
| Category: | PC , Polycarbonate |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKANATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Av2iB4_TEKANATE-G7020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TEKANATE™ G7020 is a Polycarbonate (PC) product. It can be processed by injection molding and is available in Asia Pacific. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 62.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 140 | % | ASTM D638 |
| Flexural Modulus | 2080 | MPa | ASTM D790 |
| Flexural Strength | 90.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | > 130 | °C | |
| 1.8 MPa, Unannealed | > 130 | °C | |
| Peak Melting Temperature | 270 to 300 | °C | ASTM D2133 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 110 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® HTN FE8200 NC010 | DuPont Performance Polymers | PPA | Zytel® HTN |
| Gallonprene® GP520-6011 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina CLEAR PVC COMPOUND -E 80/266-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ALCOM® PC 740/48 CC1124-13LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| LNP™ THERMOCOMP™ KF004 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |