Royalite R540M
| Category: | ABS+PVC , Acrylonitrile Butadiene Styrene + PVC |
| Manufacturer: | Spartech Plastics |
| Trademark: | Royalite |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Autr0D_Royalite-R540M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Royalite R540M offers a unique ABS/PVC product that has inherent flame retardancy as well as easy processing characteristics. It provides good weatherability, excellent low temperature impact strength, outstanding chemical resistance and moldability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 83 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 32.8 | MPa | ASTM D638 |
| Flexural Modulus | 1900 | MPa | ASTM D790 |
| Flexural Strength | 49.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 400 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| Dart Drop Impact | ASTM D3029 | ||
| -40°C, 3.18 mm | 36.2 | J | ASTM D3029 |
| 23°C, 3.18 mm | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 67.2 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 78.3 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (2.16 mm) | V-0 5VA | UL 94 |
| Additional Information |
|---|
| Weather Rating, Grey/Black: f1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 1.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 182 - 185 | °C | |
| Middle Temperature | 188 - 191 | °C | |
| Front Temperature | 191 - 193 | °C | |
| Nozzle Temperature | 188 - 193 | °C | |
| Processing (Melt) Temp | 207 - 213 | °C | |
| Mold Temperature | 26.7 - 37.8 | °C | |
| Injection Pressure | 6.89 - 10.3 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.517 | MPa | |
| Screw Speed | 30 - 40 | rpm | |
| Clamp Tonnage | 3.4 - 4.1 | kN/cm² | |
| Cushion | 3.30 - 6.35 | mm |
| Injection instructions |
|---|
| Hold Pressure: 50% to 75% Injection Pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME PP SPEXP55 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| TEREZ PA 6 7200 TF 20 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| ZEONOR® 1060R | Zeon Corporation | COP | ZEONOR® |
| POCAN® B 1501 000000 | LANXESS GmbH | PBT | POCAN® |
| Rotuba CAP CP808 (18% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |