Torayca® A630T-10V
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torayca® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AuZw9d_Torayca-A630T-10V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torayca® A630T-10V is a Polyphenylene Sulfide (PPS) product filled with 10% carbon fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.80 | % | |
| Flow : 3.00 mm 2 | 0.20 | % | |
| PV Limit | Suzuki Method | ||
| vs. S45C | 0.90 | MPa·m/s | |
| vs. SUS | 0.70 | MPa·m/s |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Amount of Wear 3 | Suzuki Method | ||
| vs. S45C | 3.30 | mg/hr | |
| vs. SUS | 1.50 | mg/hr | |
| Coefficient of Friction 4 | Suzuki Method | ||
| vs. S45C | 0.200 | ||
| vs. SUS | 0.0400 | ||
| Tensile Stress (23°C) | 157 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.4 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 232 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.2 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature | 278 | °C | DSC |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 1MPa, 0.33 m/s |
| 4 . | 1MPa, 0.33 m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-757G J08 | CHI MEI CORPORATION | ABS | POLYLAC® |
| Tenopom® POM B3 G25 NTLA010 PR316 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| UNITIKA Nylon 66 A175G15 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| Cellophane™ XS600 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Hostacom MT8220 | LyondellBasell Industries | PP Copolymer | Hostacom |