KumhoSunny ASA XC230-HW
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Atuodg_KumhoSunny-ASA-XC230-HW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASA XC230-HW has excellent weather resistance,so it can keep stable proerty by exposing to UV-light,wet,rainy or ozone in long term without painting. Application: It is especially suitable for using out-door and widely used in automible,commodity and outside decoration materials,etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 to 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 15 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Flexural Stress 2 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength 4(23°C) | 65 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength 5(23°C) | 13 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed) | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 103 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 95.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 245 to 260 | °C | |
| Nozzle Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Condition: 4 J |
| 4 . | Condition: 4 J |
| 5 . | Condition: 5.5 J |
| 6 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4799 X 115376 C | RTP Company | PTT | RTP |
| Thermoset Plastics DC-232 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Fluon® PTFE G340 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| Hax™ HF 045/16M | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| KRATON® D1116 E | Kraton Polymers LLC | SBS | KRATON® |