Bio-Flex® F 6513
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AtL6gn_Bio-Flex-F-6513.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bio-Flex® F 6513 Biodegradable compound for injection moulding. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 - 5.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 3.00 - 5.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 46.0 | MPa | ISO 527-2 |
| Fracture | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 22 | % | ISO 527-2 |
| Flexural Modulus | 2790 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 63.0 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | 4.8 | % | ISO 527 |
| Flexural Strain at Break | No Break | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 150 - 170 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 150 | °C | |
| Middle Temperature | 160 | °C | |
| Front Temperature | 175 | °C | |
| Nozzle Temperature | 190 | °C | |
| Mold Temperature | 25.0 - 40.0 | °C |
| Injection instructions |
|---|
| Holding pressure level: 40 - 60%Melt cushion (of volume): < 10%Cooling time: 15 secmax. Dwell time: 300 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF20-60 XE-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Durepol® PBT A3 G30 PRTA011 BT304 MSP | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| Polifil® Nylon 627LP | The Plastics Group | Nylon 66 | Polifil® Nylon |
| ALTECH® PC ECO 1000/141 UV IM | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| Kepital® TX-21 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |