Sumikon® PM-9630 (Type: JK Black)
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AsX34R_SumikonPM9630TypeJKBlack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® PM-9630 (Type JK Black) is Glass fiber and Inorganic filler filled resol resin (non-anmonia phenolic) molding compound with good electronic property and heat resistance. This grade is official registered UL with V-0 (t=0.16). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.81 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.18 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.20 | % | JIS K6911 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 117 | MPa | JIS K6911 |
| Flexural Modulus | 15700 | MPa | JIS K6911 |
| Flexural Strength | 188 | MPa | JIS K6911 |
| Compressive Strength | 255 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.3 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 300 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 10 | kV/mm | JIS K6911 |
| Arc Resistance | 183 | sec | JIS K6911 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 7.0E+12 | ohms | JIS K6911 |
| -- 3 | 2.0E+12 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.160 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech PS Korad® Cap/HIPS SP-2011 | Spartech Plastics | PS (HIPS) | Spartech |
| Xuchuan XCW-30H | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Bayflex® XGT-80 (15% Glass) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| Geon™ Vinyl Rigid Extrusion 6935 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Huafon JF-A-2062 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |