CYCOLAC™ EX58 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ArzSOX_CYCOLACEX58resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High impact ABS for sheet extrusion and blow molding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.80 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2080 | MPa | ASTM D638 |
| -- | 1970 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 30.0 | MPa | ASTM D638 |
| Fracture | 30.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.1 | % | ASTM D638 |
| Yield | 2.6 | % | ISO 527-2/50 |
| Fracture 5 | 32 | % | ASTM D638 |
| Fracture | 21 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2160 | MPa | ASTM D790 |
| -- 7 | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 60.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 66.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 37 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 300 | J/m | ASTM D256 |
| 23°C | 430 | J/m | ASTM D256 |
| -30°C 10 | 23 | kJ/m² | ISO 180/1A |
| 23°C 11 | 35 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 37.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 91.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 76.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 78.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ASTM D1525 13 |
| -- | 95.0 | °C | ISO 306/B50 |
| -- | 97.0 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 14 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 100 sec^-1) | 1550 | Pa·s | ASTM D3835 |
| Extrusion instructions |
|---|
| Extrusion Blow Molding Parameters: Adapter - Zone 5 Temperature: 210 - 232 C Barrel - Zone 1 Temperature: 204 - 227 C Barrel - Zone 2 Temperature: 204 - 227 C Barrel - Zone 3 Temperature: 204 - 227 C Barrel - Zone 4 Temperature: 204 - 227 C Die Temperature: 216 - 235 C Drying Temperature: 82 - 88 C Drying Time: 4 - 5 hrs Drying Time (Cumulative): 24 hrs Extruder Feed Zone Temperature: 60 - 77 C Head - Zone 6 - Top Temperature: 216 - 232 C Head - Zone 7 - Bottom Temperature: 216 - 232 C Maximum Moisture Content: .02 % Melt Temperature (Parison): 216 - 232 C Mold Temperature: 38 - 82 C Screw Speed: 20 - 60 rpm Sheet Extrusion Parameters: Maximum Moisture Content: .02 % Melt Temperature: 216 - 260 C Roll Stack Temp - Bottom: 99 - 104 C Roll Stack Temp - Middle: 93 - 104 C Roll Stack Temp - Top: 88 - 93 C Adapter Temperature: 204 - 249 C Barrel - Zone 1 Temperature: 171 - 199 C Barrel - Zone 2 Temperature: 182 - 221 C Barrel - Zone 3 Temperature: 188 - 227 C Barrel - Zone 4 Temperature: 199 - 238 C Die Temperature: 204 - 249 C Drying Temperature: 82 - 93 C Drying Time: 4 hrs |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| 14 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALEX 01EFR002 - 6208 | AD majoris | PC | MALEX |
| Vi-Chem PVC V110-60G | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| BESTPOLUX PCG2 | Triesa Plastics | PC | BESTPOLUX |
| Hylon® N2200HL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| OTECH PVC OM7040-Molding | OTECH Corporation | PVC, Unspecified | OTECH PVC |