INNOPOL® PP CS 1-3820 MA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ar37Ud_INNOPOL-PP-CS-1-3820-MA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-3820 MA is a 20 % glass fibre filled polypropylene homopolymer compound. This grade is available in natural and custom coloured form. INNOPOL® CS 1-3820 MA is recommended for producing injection molded products, where the required properties are high strength and stiffness besides long term heat stability and excellent processability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.81 | % | ISO 294-4 |
| Flow direction | 0.50 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 5.0 | % | ISO 527-2 |
| Flexural Modulus 1 | 3450 | MPa | ISO 178 |
| Flexural Stress 2 | 92.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 25 | kJ/m² | ISO 179/1eU |
| 23°C | 39 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 133 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 190 - 230 | °C | |
| Front Temperature | 190 - 230 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Type 1A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO F-3900H | Prime Polymer Co., Ltd. | PP Homopolymer | PRIME TPO |
| SABIC® STAMAX 20YK270E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| 4DUR® 9K22730 FR3 | 4Plas | PBT | 4DUR® |
| CP PRYME® Polypropylene PPC100ZNA/3.5I-12M NAT | Chase Plastics Services Inc. | PP Impact Copolymer | CP PRYME® Polypropylene |
| FRIANYL® B3 VNGF25 V0 | Nilit Plastics | Nylon 6 | FRIANYL® |