Vydyne® M344
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AqO0nV_Vydyne-M344.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vydyne M344 is an halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016") thick. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.27 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 1.8 | -- | % | |
| Flow : 23°C, 2.00 mm | 1.3 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.80 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3500 | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 60.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield, 23°C | 5.2 | 25 | % | |
| Break, 23°C | 35 | 75 | % | |
| Flexural Modulus (23°C) | 3000 | 1400 | MPa | ISO 178 |
| Flexural Strength (23°C) | 90.0 | 43.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.2 | -- | kJ/m² | |
| 23°C | 5.5 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | -- | ||
| Notched Izod Impact Strength (23°C) | 5.0 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 186 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 250 | -- | °C | ISO 3146 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 1.0E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.0E-4 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.400 mm | 65.0 | -- | °C | |
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.400 mm | 65.0 | -- | °C | |
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 95.0 | -- | °C | |
| 3.00 mm | 95.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.400 mm | 65.0 | -- | °C | |
| 0.750 mm | 95.0 | -- | °C | |
| 1.50 mm | 95.0 | -- | °C | |
| 3.00 mm | 95.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (0.750 mm) | 1.0E+10 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 26 | -- | kV/mm | IEC 60243 |
| Arc Resistance (3.00 mm) | PLC 6 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 400 to 599 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm | V-0 | -- | ||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| 3.00 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 700 | -- | °C | |
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 725 | -- | °C | |
| Oxygen Index | 30 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Caltex PP M540SB | GS Caltex | PP Impact Copolymer | Caltex PP |
| Generic PS (MIPS) | Generic | PS (MIPS) | Generic |
| POLIMAXX 1111NXGA6 | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |
| EMERGE™ PC/ABS 7700 EU | Trinseo | PC+ABS | EMERGE™ |
| ULTEM™ 2310 resin | SABIC Innovative Plastics | PEI | ULTEM™ |