Telcar® TELC-1000-105 Datasheet,TPE,Teknor Apex Company-SHANGHAI SUSHENG

Message
Telcar TELC 1000-105 is a general purpose thermoplastic elastomer designed for the industrial market. Telcar TELC 1000-105 is a high hardness, low density grade suitable for both injection molding and extrusion.

General Information
Features	Low Specific Gravity Without Fillers Low density Low liquidity High hardness
Uses	Industrial application General
Appearance	Translucent
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.890	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	4.5	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 5 sec)	59		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus	655	MPa	ASTM D790

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
Transverse flow : 100% strain	11.0	MPa	ASTM D412
Flow : 100% strain	13.1	MPa	ASTM D412
Tensile Strength			ASTM D412
Transverse flow : Fracture	13.4	MPa	ASTM D412
Flow : Fracture	15.9	MPa	ASTM D412
Tensile Elongation			ASTM D412
Transverse flow : Fracture	290	%	ASTM D412
Flow : Fracture	230	%	ASTM D412
Tear Strength - Across Flow ¹	121	kN/m	ASTM D624
Compression Set			ASTM D395
23°C, 22 hr	54	%	ASTM D395
70°C, 22 hr	74	%	ASTM D395
90°C, 70 hr	93	%	ASTM D395

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air			ISO 188
110°C, 1008 hr	3.4	%	ISO 188
125°C, 168 hr	1.8	%	ISO 188
Change in Tensile Strain at Break in Air			ISO 188
110°C, 1008 hr	-34	%	ISO 188
125°C, 168 hr	-19	%	ISO 188
Change in Shore Hardness in Air (support d, 110°C, 1008 hr)	3.2		ISO 188

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	-55.0	°C	ASTM D746
RTI Elec	50.0	°C	UL 746
RTI Imp	50.0	°C	UL 746
RTI	50.0	°C	UL 746

Flammability	Nominal Value		Test Method
Flame Rating (0.750 mm, All Colors)	HB		UL 94

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 206 sec^-1)	378	Pa·s	ASTM D3835

Legal statement
The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Legal statement

The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Injection	Nominal Value	Unit
Rear Temperature	171 - 193	°C
Middle Temperature	177 - 199	°C
Front Temperature	182 - 204	°C
Nozzle Temperature	188 - 210	°C
Processing (Melt) Temp	188 - 210	°C
Mold Temperature	25.0 - 65.6	°C
Injection Pressure	1.38 - 6.89	MPa
Injection Rate	Moderate-Fast
Back Pressure	0.172 - 0.345	MPa
Screw Speed	50 - 100	rpm
Cushion	3.81 - 25.4	mm

Injection instructions
Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C).

Extrusion	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Cylinder Zone 1 Temp.	166 - 188	°C
Cylinder Zone 2 Temp.	171 - 193	°C
Cylinder Zone 3 Temp.	177 - 199	°C
Cylinder Zone 5 Temp.	182 - 204	°C
Die Temperature	190 - 210	°C

Extrusion instructions
螺杆转速30 - 100 rpm

Note Message
1 .	C mould

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Teknor Apex Company
Trademark:	Telcar®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Apb35y_Telcar-TELC-1000-105.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Mapex AN0320SN02	Ginar Technology Co., LTD.	Nylon 6	Mapex
Qenos PE GM7655	Qenos Pty Ltd	HDPE, HMW	Qenos PE
Abstron BL60	Bhansali Engineering Polymers Limited	ABS	Abstron
Baydur® 726 IBS (55 pcf)	Covestro - PUR	PUR-MDI	Baydur®
AVALON® 65 AE	Huntsman Corporation	TPU-Polyester	AVALON®