PAmpellonne® 617
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Politem Plastik Ltd. |
| Trademark: | PAmpellonne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AomsEm_PAmpellonne-617.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| All Politem Plastik Polyamide Resins are recycled from Post Industrial Fiber Waste Streams |
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Ash Content | 0.10 | % | ISO 3451-4 |
| Moisture | 0.10 to 0.30 | % | ISO 15512/B |
| Relative Viscosity 1 | 2.70 to 2.90 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| DSC Analysis | > 99 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 to 4000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 to 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 5.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 to 7.0 | kJ/m² | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 220 to 225 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Formic |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Nylon A4TR02 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| Sindustris ABS LHF491NS | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Capilene® TG 50 | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| Lucel® GC240 | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |
| Polychim HB12XF | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |