Fiberfil® PP-60/VO/NH
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AoV1Pm_Fiberfil-PP-60-VO-NH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®PP-60/VO/NH is a polypropylene homopolymer (PP Homopoly) material,. This product is available in North America,. Fiberfil®The main features of PP-60/VO/NH are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 - 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 1.3 - 1.7 | % | ASTM D955 |
| 6.35 mm | 1.8 - 2.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 - 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2310 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 20.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 2240 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 33.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 85.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 73.9 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 182 - 199 | °C | |
| Middle Temperature | 193 - 210 | °C | |
| Front Temperature | 188 - 204 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 193 - 216 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Slow to Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SSZ7209 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| VITAMIDE® BI14BK8509 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Badamid® PA610 GF30 | Bada AG | Nylon 610 | Badamid® |
| HOPELEN FR-160 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| VisiJet® FTX Gray | 3D Systems | Unspecified | VisiJet® |