Bergadur™ PB40 G30 BK097
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergadur™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Anw3Zm_Bergadur-PB40-G30-BK097.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced PBT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 - 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 130 | MPa | ISO 527-2 |
| Flexural Modulus | 8200 | MPa | ISO 178 |
| Flexural Stress | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.2 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 210 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 75.0 - 95.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS VL-1 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| SLOVAMID® 66 GF 10 FRA 3 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| VECTRA® B230 | Celanese Corporation | LCP | VECTRA® |
| Nylene® 132 HSL | Custom Resins Group | Nylon 66 | Nylene® |
| ELASTOSIL® R 502/75 | Wacker Chemie AG | Silicone | ELASTOSIL® R |