Epiall® 1908B-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Epiall® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Amnk2s_Epiall-1908B-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Epiall 1908B-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.98 | g/cm³ | ASTM D792 |
| Apparent Density | 0.90 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 70 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 76.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 15900 | MPa | ASTM D790 |
| Flexural Strength (Break) | 145 | MPa | ASTM D790 |
| Compressive Strength | 180 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, Compression Molded) | > 282 | °C | ASTM D648 |
| CLTE - Flow | 3.7E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 12 | kV/mm | ASTM D149 |
| Dielectric Constant 1(1 MHz) | 4.50 | ASTM D2520 | |
| Dissipation Factor 2(1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index | 500 | V | IEC 60112, ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.40 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Wet |
| 2 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Alpha PVC GW 2462-H VW1 NAT LCF | AlphaGary | PVC, Semi-Rigid | Alpha PVC |
| Axiall PVC 50897 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| INVISION™ GX 5135DG5M2C | A. Schulman Inc. | TPE | INVISION™ |
| Karina WHITE PVC COMPOUND -E 837-10/168-A-ERYB-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pujie CPE-135C | Zhanhua Pujie Chemical Technology Co.,Ltd | CPE | Pujie |