Generic HDPE
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ak8YV5_Generic-HDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic HDPE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.945 - 0.975 | g/cm³ | ASTM D792 |
| 23°C | 0.944 - 0.976 | g/cm³ | ISO 1183 |
| -- | 930 | kg/m³ | ISO 1183 1 |
| -- | 0.942 - 0.966 | g/cm³ | ASTM D1505 |
| -- | 0.945 - 0.963 | g/cm³ | ASTM D4883 |
| Apparent Density | |||
| -- | 0.55 - 0.61 | g/cm³ | ASTM D1895 |
| -- | 0.46 - 0.55 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.020 - 1.8 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.030 - 10 | g/10 min | ISO 1133 |
| Melt volume-flow rate | 0.646 | cm³/10min | ISO 1133 2 |
| Spiral Flow | 18.8 - 74.5 | cm | |
| Molding Shrinkage | |||
| Flow : 23°C | 0.018 - 3.0 | % | ASTM D955 |
| Transverse flow : 23°C | 0.96 - 2.5 | % | ASTM D955 |
| 23°C | 1.4 - 2.0 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.010 - 0.10 | % | ASTM D570 |
| Environmental Stress-Cracking Resistance (23°C) | 0.500 - 1130 | hr | ASTM D1693 |
| Viscosity Number (Reduced Viscosity) (23°C) | 157.8 - 398.3 | ml/g | ISO 1628 |
| Carbon Black Content | 1.9 - 2.7 | % | ASTM D1603 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 45 - 60 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 59 - 71 | ASTM D2240 | |
| 23°C | 57 - 70 | ISO 868 | |
| Ball Indentation Hardness | 39.0 - 58.5 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 269 - 1280 | MPa | ASTM D638 |
| 23°C | 833 - 1360 | MPa | ISO 527-2 |
| -- | 1110 | MPa | ISO 527-2 3 |
| Tensile Strength | |||
| Yield, 23°C | 16.9 - 31.7 | MPa | ASTM D638 |
| Yield, 23°C | 20.7 - 31.6 | MPa | ISO 527-2 |
| Yield | 25.1 | MPa | ISO 527-2 4 |
| Fracture, 23°C | 13.9 - 38.7 | MPa | ASTM D638 |
| Fracture, 23°C | 14.5 - 36.1 | MPa | ISO 527-2 |
| Limit, 23°C | 23.9 - 33.0 | MPa | ASTM D638 |
| 23°C | 10.0 - 29.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.0 - 27 | % | ASTM D638 |
| Yield, 23°C | 2.5 - 17 | % | ISO 527-2 |
| Yield | 11 | % | ISO 527-2 5 |
| Fracture, 23°C | 4.0 - 1000 | % | ASTM D638 |
| Fracture, 23°C | 6.0 - 1000 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 675 | MPa | ISO 899-1 |
| 1000 hr | 293 | MPa | ISO 899-1 |
| Apparent Bending Modulus (23°C) | 597 - 1180 | MPa | ASTM D747 |
| Flexural Modulus | |||
| 23°C | 695 - 1730 | MPa | ASTM D790 |
| 23°C | 777 - 1620 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 18.5 - 42.3 | MPa | ASTM D790 |
| 23°C | 19.0 - 32.0 | MPa | ISO 178 |
| Yield, 23°C | 26.1 - 31.9 | MPa | ASTM D790 |
| Coefficient of Friction | 0.20 - 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 10 - 47 | µm | |
| Film Puncture Resistance | 2.76 | J/cm³ | |
| secant modulus | |||
| MD | 578 - 1280 | MPa | ASTM D882 |
| TD | 636 - 1490 | MPa | ASTM D882 |
| 23°C | 400 - 800 | MPa | ISO 527-3 |
| Tensile Strength | |||
| MD : Yield | 20.3 - 40.7 | MPa | ASTM D882 |
| TD : Yield | 21.4 - 30.6 | MPa | ASTM D882 |
| Yield, 23°C | 19.0 - 32.2 | MPa | ISO 527-3 |
| MD : Fracture | 16.7 - 100 | MPa | ASTM D882 |
| TD : Fracture | 16.8 - 62.2 | MPa | ASTM D882 |
| Fracture, 23°C | 25.4 - 67.0 | MPa | ISO 527-3 |
| 23°C | 19.9 - 75.1 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| MD : Fracture | 240 - 660 | % | ASTM D882 |
| TD : Fracture | 2.0 - 950 | % | ASTM D882 |
| Fracture, 23°C | 240 - 800 | % | ISO 527-3 |
| Dart Drop Impact | |||
| 23°C | 7.0 - 350 | g | ASTM D1709 |
| 23°C | 40 - 350 | g | ISO 7765-1 |
| Elmendorf Tear Strength | |||
| MD | 0.40 - 40 | g | ASTM D1922 |
| TD | 3.0 - 360 | g | ASTM D1922 |
| -- | 0.065 - 0.84 | N | ISO 6383-2 |
| Water Vapor Transmission Rate | 1.9 - 14 | g/m²/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 2.2 - 26 | kJ/m² | ISO 179 |
| 23°C | 28.6 | kJ/m² | ISO 179/1eA 6 |
| Charpy Unnotched Impact Strength (23°C) | 2.0 - 24 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 1.0 - 510 | J/m | ASTM D256 |
| 23°C | 1.9 - 31 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 7.0 - 1100 | J/m | ASTM D256 |
| Tensile Impact Strength | |||
| 23°C | 40.4 - 345 | kJ/m² | ASTM D1822 |
| 23°C | 58.9 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 63.5 - 81.9 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 65.0 - 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 36.7 - 81.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 41.0 - 48.5 | °C | ISO 75-2/A |
| 1.8 MPa | 61.5 | °C | ISO 75-2 7 |
| Brittleness Temperature | |||
| -- | -82.2 - -59.8 | °C | ASTM D746 |
| -- | -70.5 - -60.0 | °C | ISO 974 |
| Vicat Softening Temperature | |||
| -- | 121 - 130 | °C | ASTM D1525 |
| -- | 69.3 - 130 | °C | ISO 306 |
| 50°C/h, B (50N) | 66.6 | °C | ISO 306 8 |
| Melting Temperature | |||
| -- | 127 - 137 | °C | |
| -- | 128 - 135 | °C | DSC, ASTM D3418, ISO 3146 |
| -- | 130 - 136 | °C | ISO 11357-3 |
| -- 9 | 146 | °C | ISO 11357-3 10 |
| Peak Crystallization Temperature (DSC) | |||
| -- | 113 - 132 | °C | ASTM D3418 |
| -- | 131 - 132 | °C | ISO 3146 |
| CLTE - Flow | 7.1E-5 - 2.0E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat (23°C) | 1840 - 2300 | J/kg/°C | ASTM C351 |
| Thermal Conductivity (23°C) | 0.48 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 40 - 2.5E+13 | ohms | ASTM D257 |
| -- | 1.6E+2 - 2.5E+12 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 10 - 2.5E+18 | ohms·cm | ASTM D257 |
| 23°C | 10 - 1.3E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 20 - 30 | kV/mm | ASTM D149 |
| 23°C | 20 - 150 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.24 - 2.60 | ASTM D150 | |
| 23°C | 2.32 - 2.56 | ASTM D1531 | |
| 23°C | 2.32 - 2.35 | IEC 60250 | |
| 1 MHz | 2.30 | IEC 60250 11 | |
| Dissipation Factor | |||
| 23°C | 2.0E-5 - 2.7E-4 | ASTM D150 | |
| 23°C | 5.7E-5 - 3.0E-4 | ASTM D1531 | |
| 23°C | 5.0E-5 - 4.1E-4 | IEC 60250 | |
| 1 MHz | 3.0E-4 | IEC 60250 12 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 5 - 120 | ASTM D2457 | |
| Haze | 3.0 - 82 | % | ASTM D1003 |
| Yellowness Index | 0.0 - 4.0 | YI | ASTM D1925 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.8 - 85.0 | °C | |
| Drying Time | 1.9 - 3.1 | hr | |
| Suggested Max Moisture | 0.030 - 0.21 | % | |
| Rear Temperature | 185 - 234 | °C | |
| Middle Temperature | 184 - 248 | °C | |
| Front Temperature | 224 - 248 | °C | |
| Nozzle Temperature | 234 - 246 | °C | |
| Processing (Melt) Temp | 180 - 251 | °C | |
| Mold Temperature | 18.5 - 46.9 | °C | |
| Injection Pressure | 76.8 - 86.5 | MPa | |
| Back Pressure | 0.138 - 7.75 | MPa | |
| Screw Speed | 53 - 56 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic HDPEThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 91.3 | °C | |
| Drying Time | 1.9 - 3.1 | hr | |
| Cylinder Zone 1 Temp. | 149 - 221 | °C | |
| Cylinder Zone 2 Temp. | 168 - 203 | °C | |
| Cylinder Zone 3 Temp. | 163 - 221 | °C | |
| Cylinder Zone 4 Temp. | 174 - 233 | °C | |
| Cylinder Zone 5 Temp. | 178 - 233 | °C | |
| Adapter Temperature | 150 - 253 | °C | |
| Melt Temperature | 190 - 218 | °C | |
| Die Temperature | 181 - 233 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic HDPEThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | 10 °C/min |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Impet® 340R | Celanese Corporation | PET | Impet® |
| LNP™ THERMOCOMP™ DC0049XF compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Politen® G2HC10 | ITEN INDUSTRIES | Polyester Alloy | Politen® |
| POLYfill PPC T1030 | Polykemi AB | PP Copolymer | POLYfill |
| Plavis® C | Comco Nylon GmbH | PI, TP | Plavis® |