| Starflam BFR200Y is Unfilled, Halogen Free and Red Phosphorous Free Flame Retardant Polyamide 6 Injection Molding Resin |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.80 to 1.2 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 9.0 | % | |
| Equilibrium, 23°C, 50% RH | 2.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 78.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.7 | % | |
| Break | 5.6 | % | |
| Flexural Modulus 2 | 3100 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | > 100 | kJ/m² | |
| 23°C | > 100 | kJ/m² | |
| Notched Izod Impact Strength 5 | ISO 180/1A | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 190 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 75.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 205 | °C | ISO 306/B50 |
| -- | 200 | °C | ISO 306/B120 |
| Ball Pressure Test 7(125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.5E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.0E-5 | cm/cm/°C | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 100 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 8 | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 7.8E-3 | ||
| 60 Hz | 7.8E-3 | ||
| 1 MHz | 0.019 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 120*10*4 |
| 7 . | 125°C ±2°C |
| 8 . | ROA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4885 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Prime Polypro™ J-452HP | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| Toler PE PE862 | Toler Chemical, Inc | HDPE | Toler PE |
| Di-Pak™ R-4528/30 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| ESTOPLAST EP 4020WW26 | Ester Industries Ltd. | PBT | ESTOPLAST EP |