LNP™ STAT-LOY™ 63000CTU compound
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AhxAhm_LNP-STAT-LOY-63000CTU-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A permanent antistatic PC-Alloy compound that features transparency, UV cut, and superior cleanliness for advanced semiconductor packaging applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.60 | % | |
| Across Flow | 0.60 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1160 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 36.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 200 | % | ASTM D638 |
| Flexural Modulus | 1210 | MPa | ASTM D790 |
| Flexural Strength 3(Break, 50.0 mm Span) | 53.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 69 | kJ/m² | ISO 179/2C |
| Notched Izod Impact (23°C) | 500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 83.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 74.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 to 5.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+11 to 5.0E+12 | ohms·cm | ASTM D257 |
| Static Decay 4 | 2.0 | sec | FTMS 101B |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 35.0 | % | Internal Method |
| Haze (2540 µm) | 10 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 95.0 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 225 to 240 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUPLENE® R37Y | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Karina BLUE COLOR CONCENTRATE -E 06/ 40-RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ DL0039EF compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Plaslube® AC-81/TF/20/Natl | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |
| Osterlene® LLB0918SA | Osterman & Company | LLDPE | Osterlene® |