HIPOL™ J300
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Mitsui Chemicals, Inc. |
| Trademark: | HIPOL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AgZhhG_HIPOL-J300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIPOL™ J300 is a Polypropylene Homopolymer (PP Homopolymer) material. It is available in Asia Pacific for injection molding. Important attributes of HIPOL™ J300 are:
Typical application of HIPOL™ J300: Engineering/Industrial Parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.4 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 37.3 | MPa | |
| Break | 34.3 | MPa | |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C | 29 | J/m | |
| 23°C | 59 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 110 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C | |
| Vicat Softening Temperature | 155 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.57 mm, ALL) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 260 | Taro Plast S.p.A. | Nylon 66/6 | TAROMID A |
| Baoding 67I85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| FM® 410-1 | Cytec Industries Inc. | Epoxy | FM® |
| ENFLEX VU-420-60A | Ravago Group | PP+EPDM | ENFLEX |
| TECHNYL® C 52G2 MV25 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |