NEOFLON™ EFEP RP-5000AS

Category:	Fluoropolymer , Fluoropolymer
Manufacturer:	DAIKIN AMERICA, INC.
Trademark:	NEOFLON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	AfP08c_NEOFLON-EFEP-RP-5000AS.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

EFEP RP-5000AS is a static dissipating fluoropolymer specifically designed for the automotive industry. This resin combines the excellent physical and chemical properties derived from ETFE together with a low processing temperature that is more compatible with engineering resins and conventional thermoplastic polymers. EFEP RP-5000AS adheres well to many kinds of plastics without adhesive or etching.

EFEP RP-5000AS can be easily co-extruded into multi-layer tubing and offers the following advantages for automotive applications:

Very good permeation resistance to hydrocarbons

Excellent chemical resistance

Improved heat aging resistance

Co-extrusion with other resins (nylons, EVOH, modified PE, and ETFE) without adhesive or etching

Superior adhesion strength

Cold impact resistance

General Information
Features	Antistatic property Good heat aging resistance Good adhesion Low temperature impact resistance Good chemical resistance Hydrocarbon resistance
Uses	Pipe fittings Application in Automobile Field Fuel line
Forms	Particle
Processing Method	Co-extrusion molding Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.76	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (265°C/5.0 kg)	2.0 - 8.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	29.0 - 50.0	MPa	ASTM D638
Tensile Elongation (Break)	200 - 350	%	ASTM D638
Flexural Modulus	1400	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	195	°C	DSC

Additional Information	Nominal Value	Unit
Permeation Resistance - Average ¹(60°C)	6.5	g·mm/m²/atm/24 hr

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	260	°C
Cylinder Zone 3 Temp.	260	°C
Cylinder Zone 5 Temp.	260	°C
Adapter Temperature	265	°C
Die Temperature	280	°C

Extrusion instructions
Cylinder Diameter: 30 mmScrew L/D: 24Compression Ratio: 3Die I.D.: 16 mmTip O.D.: 12 mm

Note Message
1 .	Ce-10

Resin Grade	Manufacturer	Category	Trademark
SABIC® PPcompound 2401-1	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
New-prene™ 9185N	Total Polymer Vision (Suzhou) Co., LTD	PP+EPDM	New-prene™
Kumho SBR 1502	Korea Kumho Petrochemical Co., Ltd.	SBR, Emulsion	Kumho SBR
ICORENE® 1339	ICO Polymers EMEA, A Division of A. Schulman	HDPE	ICORENE®
LNP™ THERMOCOMP™ Lexan_LGK5030 compound	SABIC Innovative Plastics	PC	LNP™ THERMOCOMP™