Sindustris PP EH5151H
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AcxfGI_Sindustris-PP-EH5151H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PP EH5151H is a Polypropylene material filled with 15% mineral. It is available in Asia Pacific for injection molding. Primary attribute of Sindustris PP EH5151H: High Flow. Typical application of Sindustris PP EH5151H: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 100 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.1 to 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 10 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 1770 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 36.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -10°C, 6.40 mm | 20 | J/m | |
| 23°C, 6.40 mm | 39 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 130 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P40B01 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| UNIPA® lm | Nytef Plastics, Ltd. | Nylon 612 | UNIPA® |
| Kepital® F30-34 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| LubriOne™ AT-000/20T Black | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| TechnoElast V A7000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |