SMOKEGUARD™ O 303 NATURAL
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | AlphaGary |
| Trademark: | SMOKEGUARD™ O |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AcgzoD_SMOKEGUARD-O-303-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SMOKEGUARD O-303 IS 90C DEGREE, ZERO HALOGEN, PLENUM CABLE INSULATION SKIN COMPOUND. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 - 1.49 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 6.7 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 62 - 68 | ASTM D2240 | |
| Shaw D, 15 seconds | 52 - 58 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (0.762 mm) | 12.1 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 25 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 1(121°C, 168 hr) | 5.0 | % | UL Unspecified |
| Change in Ultimate Elongation in Air 2(121°C, 168 hr) | 25 | % | UL Unspecified |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -8.00 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant | ASTM D150 | ||
| 23°C, 100 MHz | 3.12 | ASTM D150 | |
| 23°C, 350 MHz | 3.12 | ASTM D150 | |
| 23°C, 600 MHz | 3.13 | ASTM D150 | |
| 23°C, 1.00 GHz | 3.09 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 23°C, 100 MHz | 9.0E-4 | ASTM D150 | |
| 23°C, 350 MHz | 8.0E-4 | ASTM D150 | |
| 23°C, 600 MHz | 1.1E-3 | ASTM D150 | |
| 23°C, 1.00 GHz | 8.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 35 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 171 | °C | |
| Cylinder Zone 2 Temp. | 177 | °C | |
| Cylinder Zone 3 Temp. | 182 | °C | |
| Cylinder Zone 4 Temp. | 188 | °C | |
| Adapter Temperature | 193 | °C | |
| Melt Temperature | 193 - 204 | °C | |
| Die Temperature | 193 | °C |
| Extrusion instructions |
|---|
| Screw Design: General purpose screwScreen Pack: 40/60/40 or 40/80/40 |
| Note Message | |
|---|---|
| 1 . | Thickness: 30 mil |
| 2 . | Thickness: 30 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SE-110M68 | SHIN-A T&C | Epoxy | SHIN-A |
| Tuffak® S | Altuglas International of Arkema Inc. | PC | Tuffak® |
| Witcom POM-C 4L3 | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| Plaskon NXG-1LAR | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| ULTEM™ 2200R resin | SABIC Innovative Plastics | PEI | ULTEM™ |