TECHNYL® C 236 V35 Black Z is a polyamide 6 reinforced with 35% of glass fiber, with improved impact resistance, for injection moulding. This grade offer a high impact strength and good mechanical properties.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 35% filler by weight
Additive	Impact modifier
Features	Impact resistance, good Good liquidity Good demoulding performance
Uses	Wire and cable applications Industrial application Consumer goods application field
Agency Ratings	EC 1907/2006 (REACH) UL QMFZ2
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Injection molding
Resin ID (ISO 1043)	PA6-GF35

Physical	Nominal Value	Unit	Test Method
Density	1.41	g/cm³	ISO 1183/A
Water Absorption (23°C, 24 hr)	0.90	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	9700	MPa	ISO 527-2/1A
Tensile Stress (Break, 23°C)	160	MPa	ISO 527-2/1A
Tensile Strain (Break, 23°C)	3.6	%	ISO 527-2
Flexural Modulus (23°C)	8600	MPa	ISO 178
Flexural Stress (23°C)	243	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	15	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	86	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	222	°C	ISO 11357-3

Flammability	Nominal Value		Test Method
Flame Rating (0.8 mm)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	230 - 235	°C
Middle Temperature	235 - 240	°C
Front Temperature	240 - 250	°C
Mold Temperature	60 - 90	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C.

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C.

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Acfsvl_TECHNYLC236V35BLACKZ.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Ravago Compounds HMP-306 (Roto)	Ravago Manufacturing Americas, LLC	MDPE	Ravago Compounds
Novalloy-B B14MO	Daicel Polymer Ltd.	ABS+PBT	Novalloy-B
Nylene® 5105 HS	Custom Resins Group	Nylon 66	Nylene®
Evoprene™ 3274	AlphaGary	SBS	Evoprene™
TECHNYL STAR® AFX 216 V60 GREY 2327	Solvay Engineering Plastics	Nylon 66	TECHNYL STAR®