KPOL-PP K-PPC 40.0

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	AbixnO_KPOL-PP-K-PPC-40-0.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Heterophasic Copolymer

Characteristics

The KPOL® resin is high impact block copolymer which has more ethylene contents than normal block copolymer, designed for injection molding applications.

Characteristics : High Stiffness, Impact Strength, High flow.

Applications

KPOL® K-PPC 40.0 is a heterofhasic copolymer of high fluidity, which provides high rigidity and resistance to the average impact. By presenting excellent flavors, is recommended for use in packaging of food products that require low transfer of odor and taste. Injection Molding of Automobile applications, large container, Industrial parts for electronic, toys, thin-walled rigid containers, home utilities and others.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant Block Copolymer Food Contact Acceptable Good Impact Resistance Good Stiffness High Flow High Rigidity Low Odor Transfer Low Taste Transfer Nucleated
Uses	Automotive Applications Containers Electrical/Electronic Applications Household Goods Industrial Parts Thin-walled Parts Toys
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	40	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	88		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	27.0	MPa	ASTM D638
Tensile Elongation ²(Break)	7.0	%	ASTM D638
Flexural Modulus - 1% Secant	1300	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (-20°C)	35	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	108	°C	ASTM D648
Vicat Softening Temperature	150	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom SCR1-5015	Spartech Polycom	ABS	Spartech
Dynaflex™ G7940-9 NSFG	PolyOne Corporation	TPE	Dynaflex™
DynaPath™ 3230-CF	Polymer Dynamix	PEEK	DynaPath™
Sumiliteresin® PR-8000	SBHPP	Phenolic	Sumiliteresin®
XYLEX™ X7507 resin	SABIC Innovative Plastics	PC+Polyester	XYLEX™