ELIX™ ABS E310
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ELIX Polymers, S. L. |
| Trademark: | ELIX™ ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AbFH5X_ELIX-ABS-E310.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Elix ABS E310 Extrusion grade, high impact resistance, high gloss surfaces |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.50 to 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 43.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 2.5 | % | ISO 527-2 |
| Break, 23°C | > 15 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 100 | kJ/m² | |
| 23°C | 140 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 21 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.10 | ||
| 23°C, 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 5.0E-3 | ||
| 23°C, 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index (Solution A) | 575 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 700 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 70.0 | °C | |
| Injection Velocity | 240 | mm/sec | ISO 294 |
| Note Message | |
|---|---|
| 1 . | 60x60x2 |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8299-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Cheng Yu LD3010 Light Dispersive | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| ExxonMobil™ AP03B | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| DynaMix™ PA625-60 | Polymer Dynamix | Nylon 6 | DynaMix™ |
| PLUSTEK RA115 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |