Jackdaw PLA HS10VN6587
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Jackdaw PLA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AbCy4N_Jackdaw-PLA-HS10VN6587.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jackdaw PLA HS10VN6587 is a Polylactic Acid (PLA) product. It is available in Europe. Primary characteristic: eco-friendly/green. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 55.0 | MPa | |
| Break | 47.0 | MPa | |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 2.0 | % | |
| Break | 3.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 1 | 21.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 21 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 54.0 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 152 | °C | ASTM D2117, ISO 1218 |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7530 GK 10 GF 20 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| NEXUS ABS ABSHFL | Nexus Resin Group, LLC. | ABS | NEXUS ABS |
| Hanwha Total PP TI51H | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| HIPOLEN P® FY 6 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| LUVOCOM® 65-7712/GY | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |