XYRON™ 740V
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | XYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AazWXh_XYRON-740V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified PPE Unreinforced Flame retardant V-1 Heat resistance High |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(2.00 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 69.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 21 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2470 | MPa | ISO 178 |
| Flexural Stress (23°C) | 106 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 13 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 134 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength 3(2.00 mm) | 29 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 2.90 | ||
| 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 4.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 320 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x2 mm |
| 2 . | 4 mm |
| 3 . | Short Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7109FJ | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| Sinvicomp SRG5540 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Hyundai EP PA66 LD610 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Kumho SAN SAN 320 | Korea Kumho Petrochemical Co., Ltd. | SAN | Kumho SAN |
| LNP™ THERMOCOMP™ DB008ERP compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |