Magnobond 55-2
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Magnolia Plastics, Inc. |
| Trademark: | Magnobond |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AXnPaW_Magnobond-55-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Magnobond 55-2 is an Epoxy; Epoxide (Epoxy) product. It is available in North America. Typical application: Adhesives/Tapes. Primary characteristic: chemical resistant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.7 | MPa | ASTM D638 |
| Flexural Modulus | 2140 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Compressive Strength | 10.3 | MPa | ASTM D695 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+5 | ohms·cm | ASTM D257 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 1.0 | ||
| Resin | Mix Ratio by Volume: 1.0 | ||
| Pot Life (25°C) | 180 | min | |
| Thermoset Mix Viscosity (25°C) | 200000 | cP | ASTM D2393 |
| Demold Time (25°C) | 720 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PP TPP20AJ25UL BLACK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Flexalloy® 9200-45-BL | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| HiFill® PP GB50 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| Karina BLACK COLOR CONCENTRATE 48/ 1-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Celanex® 3400 | Celanese Corporation | PBT | Celanex® |