Elastollan® C 80 A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AX1Nk4_Elastollan-C-80-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties. Outstanding tensile strength and high elongation at break, good damping characteristics, a high resilience performance and very good wear resistance. Typical applications Spiral tubing, pneumatic tubing, round belting, technical mouldings e.g. bushes, dust caps, seals, joints, blow moulded bellows, fan belts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 3 sec) | 82 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 30.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504 | ||
| 20% Strain | 2.50 | MPa | |
| 100% Strain | 4.50 | MPa | |
| 300% Strain | 8.50 | MPa | |
| Tensile Stress | DIN 53504 | ||
| Yield 1 | 35.0 | MPa | |
| Yield | 50.0 | MPa | |
| Tensile Elongation 2(Break) | 650 | % | DIN 53504 |
| Tear Strength 3 | 65 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | |
| 70°C, 24 hr | 35 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 170 to 240 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | after storage in water for 21 days at 80°C |
| 2 . | after storage in water for 21 days at 80°C |
| 3 . | Method Bb, Angle (Nicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP 301(f2) NC713 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Next Nylon 66 Prime Series PG30-01GY | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| DINALON® B1S25 C15-4172 | Grupo Repol | Nylon 6 | DINALON® |
| FHR Polypropylene AP5106-HA | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Karina IVORY PVC COMPOUND 800-35/ 2-BYR-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |