Boltaron 9815P
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | Boltaron Performance Products |
| Trademark: | Boltaron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AWzR0S_Boltaron-9815P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Boltaron 9815P is a proprietary, fire retardant, extruded PVC/Acrylic alloy that is offered in unlimited surface textures and unlimited colors, providing designers with new ways to enhance the appearance of aircraft interior components. Because it is press laminated (not extruded), unlimited custom textures are available economically in low minimums with fast turnarounds, allowing the production of prototypes and limited runs prior to full-scale production. In addition, the sheet exhibits exceptional physical properties, most notably Izod impact resistance of 5.0 ft lbs/in (265 J/m), significantly improving the durability of thermoformed aircraft interior components, while meeting stringent FAA requirements for flammability, smoke generation and heat release. It also offers extreme formability and consistent surface quality, free of pits or inclusions. Boltaron 9815P is one of the latest additions to Boltaron's 9815 family of aircraft-rated sheet products specified by the world's leading commercial, military and private aircraft and helicopter manufacturers, carriers and interior refurbishing contractors, for thermoformed, fabricated and machined interior components of unequalled durability and appearance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 37.9 | MPa | ASTM D638 |
| Flexural Modulus | 2830 | MPa | ASTM D790 |
| Flexural Strength | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 76.7 | °C | ASTM D648 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| NBS Smoke Density | ASTM F814 | ||
| Ds, 1.5 Min | ASTM F814 | ||
| Ds, 4 Min | ASTM F814 | ||
| exothermic 1 | FAR 25.853 | ||
| 2 Min | kW·min/m² | FAR 25.853 | |
| Peak | kW/m² | FAR 25.853 | |
| Flammability | FAR 25.853 | ||
| -- 2 | Pass All | FAR 25.853 | |
| -- 3 | Pass All | FAR 25.853 |
| Additional Information |
|---|
| Thermoforming Parameters: Mold Shrinkage: 0.005 to 0.007 in/in Forming Temperature: 335 to 370°F Typical Heater Settings, Top: 30 to 50% Typical Heater Settings, Bottom: 50 to 70% Drying: Not Required |
| Note Message | |
|---|---|
| 1 . | A1 F, Part IV |
| 2 . | A1, (i) |
| 3 . | A1, (ii) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V143-70I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| NEXT REGRIND PC/ABS MG10-300 | NEXT Specialty Resins, Inc. | PC+ABS | NEXT REGRIND |
| Laticonther 80 GCE/650 | LATI S.p.A. | PPS | Laticonther |
| LUVOCOM® 80/TF/18/SI/2 - 1P | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| RTP 699 X 121289 A | RTP Company | ABS | RTP |