DIALAC® KVS700
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | DIALAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AWv88p_DIALAC-KVS700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DIALAC® KVS700 is an Acrylonitrile Ethylene Styrene (AES) material. It is available in Asia Pacific or North America for injection molding. Important attributes of DIALAC® KVS700 are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 50.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.50 to 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 102 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2250 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 37.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 62.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/Af |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.90 mm | V-0 | ||
| 2.10 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 150 to 190 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Nozzle Temperature | 170 to 210 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Pressure | 70.0 to 130 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 5.00 to 10.0 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Favorite INSTATEAR | Favorite Plastics | PE Alloy | Favorite |
| ESENTTIA 08C01T | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |
| Hostacom ERC 463N C11323 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Karina GRAY PVC COMPOUND 750-18/473-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Infino NH-1022 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |