ELITE™ 5230GC Enhanced Polyethylene Resin is produced via INSITE™ Technology from Dow. Film made from this resin offers high impact strength and good puncture resistance at moderate stretch levels for irregularly shaped loads. In addition, this resin provides excellent extensibility for higher yields on regular loads. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Film Puncture Force (20 µm) | 48.9 | N | Internal method |
| Film Puncture Resistance 1(20 µm) | 27.0 | J/cm³ | Internal method |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 9.07 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 8.39 | MPa | ASTM D882 |
| MD : Break, 20 µm | 46.0 | MPa | ASTM D882 |
| TD : Break, 20 µm | 38.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 540 | % | ASTM D882 |
| TD : Break, 20 µm | 720 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 320 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 310 | g | ASTM D1922 |
| TD : 20 µm | 510 | g | ASTM D1922 |
| Final stretch- On-Pallet testing (20.0 µm) | 330 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm) | 95 | ASTM D2457 | |
| Haze (20.0 µm) | 0.50 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 271 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film: Die gap: 20 mil (0.50mm) Melt Temperature: 520 °F (271 °C) Air Gap: 3 in. (7.6 cm) Haul Off Speed: 600 fpm (183 m/min) |
| Note Message | |
|---|---|
| 1 . | 250% pre-stretch; On-Pallet testing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 112329 | RTP Company | Unspecified | RTP |
| NYCOA Polyamide 2037 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Hostacom HBS826C | LyondellBasell Industries | PP Copolymer | Hostacom |
| Jiangsu Meilan XXMLF3-11 | Jiangsu Meilan Chemical Co., Ltd. | Fluorelastomer | Jiangsu Meilan |
| Durethan® BG 30 X W1 000000 | LANXESS GmbH | Nylon 6 | Durethan® |