TRISTAR® PC-10FR-(VIK)
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | TRISTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AUxiFN_TRISTAR-PC-10FR--VIK-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRISTAR® PC-10FR-(VIK) is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of TRISTAR® PC-10FR-(VIK) include electrical/electronic applications and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 16 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | 0.18 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | 75 | % | ASTM D1708 |
| Flexural Modulus (3.17 mm) | 2070 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.17 mm) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.17 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 121 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 137 | °C | ISO 75-2/A |
| CLTE | ASTM E831 | ||
| Flow : -40 to 95°C | 7.0E-5 | cm/cm/°C | |
| Transverse : -40 to 95°C | 6.8E-5 | cm/cm/°C | |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C 1 | 6.0E+15 | ohms·cm | |
| 90°C 2 | 3.0E+15 | ohms·cm | |
| Dielectric Strength (3.17E-6 mm) | 24 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 1 | ||
| High Voltage Arc Resistance to Ignition (HVAR) (1.60 mm) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | ||
| 3.00 mm | PLC 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 37 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 40 hr, 50% RH |
| 2 . | 96 hr, 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® M TM7ADT (Series: MC/AD1) | KRAIBURG TPE | TPE | THERMOLAST® M |
| ACCUTECH™ ABS892EV | ACLO Compounders Inc. | ABS | ACCUTECH™ |
| Chiao Fu PA66 MD212G43 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| DENKA POVAL NP-05F | Denka Company Limited | PVOH | DENKA POVAL |
| Dorlyl PVC GFC 39X14885D | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |