HAIPLEN H50 T5
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AU40l9_HAIPLEN-H50-T5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HAIPLEN H50 T5 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 25% talc. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 to 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.1 | % | |
| Flow | 1.1 | % | |
| Granule Humidity 1 | 0.050 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 30 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 | |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Pre-heater | 70.0 to 80.0 | °C | |
| Drying Time - Pre-heater | 1.0 | hr | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Daelim Po1y® TR-144 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Fainplast PVC PM 55/K | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hostaform® MT24U01 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Plexiglas® LED white 0V200 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Kumho SAN SAN 320N A | Korea Kumho Petrochemical Co., Ltd. | SAN | Kumho SAN |