LNP™ STAT-LOY™ KX01002 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ATrgxi_LNP-STAT-LOY-KX01002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-LOY KX01002 is a compound based on Acetal Copolymer resin containing Antistat. Added features include: Permanent Anti-Static. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 2.8 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 4.8 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 43.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 16 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 1600 | MPa | ISO 178 |
| Flexural Stress | 52.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 64.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+10 to 1.0E+12 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 188 to 199 | °C | |
| Front Temperature | 199 to 210 | °C | |
| Processing (Melt) Temp | 193 to 204 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP GP3203 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| ULTEM™ DT1810EV resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| YUNGSOX® PP 1600D | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| Multilon® TN-3616Q | TEIJIN LIMITED | PC+ABS | Multilon® |
| Karina CLEAR PVC COMPOUND 70/201-D-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |