CYCOLOY™ MC8002 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ATUzs9_CYCOLOYMC8002resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS, low viscosity, high impact and ductile. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2210 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 56.5 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 150 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 530 | J/m | ASTM D256 |
| 23°C | 640 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 54.2 | J | ASTM D3763 |
| 23°C, Total Energy | 61.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 107 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 110 | °C | ASTM D648 |
| CLTE - Flow (-40 to 40°C) | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 - 80 | % | |
| Rear Temperature | 249 - 288 | °C | |
| Middle Temperature | 254 - 293 | °C | |
| Front Temperature | 260 - 302 | °C | |
| Nozzle Temperature | 274 - 302 | °C | |
| Processing (Melt) Temp | 274 - 302 | °C | |
| Mold Temperature | 60 - 88 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAPYLENE GF40HKB | Sahel Chimie Co. | PP, Unspecified | SAPYLENE |
| SEETEC PP R3410 | LG Chem Ltd. | PP Random Copolymer | SEETEC PP |
| Sinvicomp SGN5819 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sylvin 2901-90 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| FRIANYL® A3 GF25 V0P1 | Nilit Plastics | Nylon 6 | FRIANYL® |