Integra™ PBT-4123
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | PolySource, LLC |
| Trademark: | Integra™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ASWmL8_IntegraPBT4123.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, High Viscosity, Natural |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 - 1.32 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 4.0 - 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.2 - 1.8 | % | ISO 294-4 |
| Viscosity Number (Reduced Viscosity) | 123.0 - 130.0 | ml/g | ISO 1628 |
| Moisture Content | % | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 49.0 - 58.6 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 180 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | > 59 | J/m | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | > 20 | kV/mm | IEC 60243-1 |
| Arc Resistance | 120 | sec | UL 746 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 240 - 265 | °C | |
| Cylinder Zone 3 Temp. | 240 - 265 | °C | |
| Cylinder Zone 5 Temp. | 240 - 265 | °C | |
| Die Temperature | 250 - 265 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VDM93-15E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TOPAS® 8007F-400 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| WPP TPO TPO-2470 UV RXF | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Karina GRAY PVC COMPOUND 806-18/364-BY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OP - PPO PPOX-210 | Oxford Polymers | PPE+PS | OP - PPO |