Taita PS 818
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taita PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AROXbs_Taita-PS-818.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taita PS 818 is a general-purpose polystyrene material,. This product is available in North America or Asia Pacific region. The processing method is extrusion. The main features of Taita PS 818 are:
The typical application field of Taita PS 818 is: thin plate |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.18 mm) | 53.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.0 | % | ASTM D638 |
| Flexural Modulus 2(23°C) | 3820 | MPa | ASTM D790 |
| Flexural Strength 3(Yield, 23°C) | 83.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 15 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 95.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 108 | °C | ASTM D1525 4 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Residual Monomer: <150 ppm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 160 - 300 | °C | |
| Middle Temperature | 160 - 300 | °C | |
| Front Temperature | 160 - 300 | °C | |
| Mold Temperature | 35.0 - 65.0 | °C | |
| Injection Pressure | 49.0 - 137 | MPa |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 2187 | RTP Company | PEI | RTP |
| Zytel® 158L NC010 | DuPont Performance Polymers | Nylon 612 | Zytel® |
| EPDM 745P | The Dow Chemical Company | EPDM | EPDM |
| 3M™ Dyneon™ Perfluoroelastomer PFE 7301BZ | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |