NORYL PPX™ PPX630F resin
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL PPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AQuHtz_NORYL-PPX-PPX630F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 2.6 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.23 | % | |
| Across Flow : 3.20 mm | 0.25 to 0.76 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 79.3 | MPa | |
| Break | 79.3 | MPa | |
| Tensile Elongation 2(Break) | 7.7 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 5560 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 100 | J/m | |
| 23°C | 170 | J/m | |
| Unnotched Izod Impact (23°C) | 830 | J/m | ASTM D4812 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 20.4 | J | |
| 23°C, Total Energy | 19.1 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 155 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 134 | °C | |
| Vicat Softening Temperature | 162 | °C | ASTM D1525 5 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.7E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 76.7 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 243 to 288 | °C | |
| Middle Temperature | 249 to 288 | °C | |
| Front Temperature | 254 to 293 | °C | |
| Nozzle Temperature | 260 to 299 | °C | |
| Processing (Melt) Temp | 260 to 299 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.051 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rynite® 545 BK504 | DuPont Performance Polymers | PET | Rynite® |
| WPP PP WPP311D | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| Nanjing Hongrui PP P860 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| Karina BLACK PVC COMPOUND 860-48/ 1-AY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucobit 1221 | Lucobit AG | PE Copolymer | Lucobit |