NOVAPOL® TF-0119 Series
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AOTLXZ_NOVAPOL-TF-0119-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TF-0119-D (1500 ppm Slip, 6300 ppm Antiblock): Thin films, premium trash bags, ice bags TF-0119-F (Process antioxidant only): Stretch wrap, blend resin |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 170 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 200 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 44.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 38.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 540 | % | |
| TD : Break, 25 µm, Blown Film | 820 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 230 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 410 | g | |
| TD : 25 µm, Blown Film | 650 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (25.0 µm) | 500 | J/cm | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 126F6 | SAX Polymers | Nylon 6 | SAXAMID™ |
| Boda BDT-LG3701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| 3M™ Dyneon™ Fluoroelastomer FC 2211 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| DynaPath™ C2010CF | Polymer Dynamix | PC | DynaPath™ |
| NHU-PPS 21150C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |