Michimid K4100GF13-03
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michimid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AO9w8W_Michimid-K4100GF13-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michimid K4100GF13-03 is a Polyamide 6 (Nylon 6) product filled with 13% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 79.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 4830 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 204 | °C | |
| 1.8 MPa, Unannealed | 185 | °C | |
| Melting Temperature | 215 | °C | ASTM D789 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 271 | °C | |
| Front Temperature | 271 | °C | |
| Nozzle Temperature | 266 | °C | |
| Processing (Melt) Temp | 277 | °C | |
| Mold Temperature | 79.4 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3991 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| THERMOLAST® K TC7HBA (Series: AD/POM) | KRAIBURG TPE | TPE | THERMOLAST® K |
| YUCLAIR® FN430 | SK Global Chemical | LLDPE | YUCLAIR® |
| Evoprene™ G 967 | AlphaGary | SEBS | Evoprene™ G |
| Karina NATURAL PVC COMPOUND 751-25/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |